| LEMBAR LAMINASI KACA EPOXY TYPE G-10 | ||||||
| JY-QC-0920A Tanggal: 19 Jul 2018 | ||||||
| Tidak. | Item Tes | Tes kondisi | Satuan | Nilai standar | Hasil Pengujian | |
| 1 | Kepadatan | ‐‐ | g/cm3 | 1.70 | 1.85 | |
| 2 | Penyerapan Kelembaban (0,187") | ASTM D-570 | % | 0,15 maks | 0,02 | |
| 3 | Tegangan Rusak Kondisi A (0,062) Kondisi D-48/50 | ASTM D-149 | kV | 45 menit 40 menit | 50 47 | |
| 4 | Permittivitas (0,187'') Kondisi A Kondisi H-24/30 Kondisi D-48/50 | ASTM D-150 | ‐‐ | 5.20 5.40 5.80 | 4.60 4.60 4.70 | |
| 5 | Kekuatan Dampak IZOD (0,187”) Panjang-Wise Melintang | ASTM D-229 | ft-lb/in Berkumai | 7.0 menit 5,5 menit | 15 10 | |
| 6 | Kekuatan Lentur (0,187”) Panjang-Bijaksana Melintang | ASTM D-790 | ksi (MPa) | 55 (380) menit 45 (311) menit | 80 (552) 70 (483) | |
| 7 | Modulus Lentur (0,187”) Panjang-Wise Melintang | ASTM D-790 | psi | ‐‐ | 2.700 2.400 | |
| 8 | Kekuatan Tarik (0,125”) Panjang-Wise | ASTM D-638 | psi | ‐‐ | 45.000 38,000 | |
| 9 | Kekuatan Kompresi | ASTM D-695 | psi | ‐‐ | 65.000 | |
| 10 | Kekerasan Rockwell M | ASTM D-785 | ‐‐ | ‐‐ | M110 | |
| 11 | Kekuatan Ikatan (0,500”) Kondisi A Kondisi E-48/50 | ASTM D-229 | lb (kg) | 2.000 menit 1.600 menit | 2.300 2.200 | |
| 12 | Kekuatan Geser (tipe pukulan, 0,125”) | ASTM D-732 | ksi (MPa) | ‐‐ | 25 (172) | |
| 13 | Indeks Suhu | ASTM D-2304 | ℃ | ‐‐ | 130 | |
| 14 | Koefisien Ekspansi Termal Linear Panjang-bijaksana Melintang | ASTM D-696 | X 10-5 in./in./°F | ‐‐ | 0,55 0,66 | |
| 15 | Peringkat mudah terbakar | UL94 | Kelas | ‐‐ | H-B | |
| 16 | Faktor Disipasi @ 1 MHz Kondisi A (0,187”) Kondisi H-24/30 Kondisi D-48/50 | ASTM D-150 | ‐‐ | 0,025 0,035 0,045 | 0,018 0,019 0,020 | |
| 17 | Kekuatan Dielektrik (Kondisi A) | ASTM D-149 | V/mil | ‐‐ | 800 | |
| 18 | Resistensi Busur (0,125") | ASTM D-495 | Detik | ‐‐ | 130 | |
| 19 | Indeks Pelacakan Komparatif (0,125") | ASTM D-3638 | V | ‐‐ | 200 | |